Phase formation and surface morphology of nickel doped Ba1-xSrxTiO3 ceramics prepared by sol-gel technique
Varied compositions in the barium strontium titanate ternary system were prepared through the slow injection sol–gel technique. Nickel dopant was introduced through a general formula of Ba1 −xSrxTi1 −yNiyO3 (x = 0·4 and 0·5; y = 0·1 and 0·4 mol-%). Thermogravimetric analysis revealed that barium str...
সংরক্ষণ করুন:
| প্রধান লেখক: | , , , , , |
|---|---|
| বিন্যাস: | প্রবন্ধ |
| প্রকাশিত: |
Maney Publishing
2014
|
| ট্যাগগুলো: |
ট্যাগ যুক্ত করুন
কোনো ট্যাগ নেই, প্রথমজন হিসাবে ট্যাগ করুন!
|
| সংক্ষিপ্ত: | Varied compositions in the barium strontium titanate ternary system were prepared through the slow injection sol–gel technique. Nickel dopant was introduced through a general formula of Ba1 −xSrxTi1 −yNiyO3 (x = 0·4 and 0·5; y = 0·1 and 0·4 mol-%). Thermogravimetric analysis revealed that barium strontium titanate gels were completely dried and stabilised at 1000°C. All barium strontium titanate samples were confirmed as phase pure perovskite by qualitative X-ray diffraction analysis in which Nickel-doped subsolidus solution was formed successfully after calcinations at 1000°C. On the other hand, there was a sign of agglomeration discernible in the prepared BST samples and the grain sizes were found to be in the range of 39·66–71·87 nm.
|
|---|