The effect of microstructure on magnetic and electrical properties of Ni0.3 Cu0.2 Zn0.5 Fe2 O4 /
The main objective of this project is to prepare six samples of Ni0.3 Cu0.2Zn0.5Fe2O4 and study the effect of microstructure towards the magnetic and electrical properties. The preparation technique for the samples relied on a solid state reaction of mixed oxides typically used for ferrite productio...
Saved in:
Main Author: | |
---|---|
Format: | Thesis Book |
Language: | English |
Published: |
2005.
|
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
LEADER | 01399nam a2200217 a 4500 | ||
---|---|---|---|
001 | vtls026923836 | ||
003 | UPM | ||
005 | 20161024001721.0 | ||
008 | 060119s2005 my a m 000 0 eng d | ||
039 | 9 | |a 200804282025 |b VLOAD |c 200602021426 |d suhaimi |y 200601190916 |z raziah | |
040 | |c UPM | ||
090 | 0 | 0 | |a FSAS 2005 84 |
100 | 0 | |a Keeven Juksuan. | |
245 | 1 | 4 | |a The effect of microstructure on magnetic and electrical properties of Ni0.3 Cu0.2 Zn0.5 Fe2 O4 / |c by Keeven bin Juksuan. |
260 | |a 2005. | ||
300 | |a 62 leaves : |b ill. ; |c 30cm. | ||
502 | |a Project paper (B.S. (Hons)) - Universiti Putra Malaysia, 2005. | ||
520 | |a The main objective of this project is to prepare six samples of Ni0.3 Cu0.2Zn0.5Fe2O4 and study the effect of microstructure towards the magnetic and electrical properties. The preparation technique for the samples relied on a solid state reaction of mixed oxides typically used for ferrite production. Six toroid samples with different sintered temperature were form. The sintering time was fixed at 10 hours for all samples. Analysis such as density, hysteresis loop, Curie temperature, permeabillity, resistivity and microstructure are done on all the samples to figure out the effect. | ||
942 | |2 lcc |c 10025 | ||
999 | |c 516117 |d 516117 | ||
952 | |0 0 |1 0 |4 0 |6 FSA S2005 00084 |7 0 |9 728360 |a 10000 |b 10000 |c 10025 |d 2016-10-24 |o FSAS 2005 84 |p 1000552813 |r 2016-10-24 |w 2016-10-24 |y 10025 |