Synthesis and surface modification of biocompatible water soluble core-shell quantum dots
In this study, the applications of CdSe/ZnS quantum dots (QDs) and its role in advanced sensings has been explored. The CdSe/ZnS was synthesized by using hot injection method with the shell ZnS layer was made using successive ionic layer adsorption and reaction (SILAR) method. The morphology of the...
Saved in:
| Main Authors: | , , , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Trans Tech Publications
2014
|
| Online Access: | http://psasir.upm.edu.my/id/eprint/35573/1/Synthesis%20and%20surface%20modification%20of%20biocompatible%20water%20soluble%20core-shell%20quantum%20dots.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | In this study, the applications of CdSe/ZnS quantum dots (QDs) and its role in advanced sensings has been explored. The CdSe/ZnS was synthesized by using hot injection method with the shell ZnS layer was made using successive ionic layer adsorption and reaction (SILAR) method. The morphology of the CdSe/ZnS QDs was studied using Transmission Electron Microscope (TEM) and the average particle size was in 10-12 nm range. The prepared QDs were optically characterized using spectrofluorescence and strong emission was observed at 620 nm. Comparison of the fluorescence emissions of CdSe/ZnS capped with various capping ligands such as L-cysteine, thioglycolic acid (TGA), mercaptopropionic acid (MPA), mercaptosuccinic acid (MSA) and mercaptoundecanoic acid (MUA) were studied. The CdSe/ZnS capped with TGA gave the strongest fluorescence emission compared to others. |
|---|