Microwave irradiation effects on hydrothermal and polyol synthesis of ZnS nanoparticles
Cubic structure of spherical ZnS nanoparticles with relatively small size and narrow size distribution were synthesized via microwave-hydrothermal (M-H) and microwave-polyol (M-P) methods from zinc acetate and thioacetamide as starting materials. Distilled water and ethylene glycol were used as solv...
Сохранить в:
| Главные авторы: | , , , , , |
|---|---|
| Формат: | Статья |
| Язык: | English |
| Опубликовано: |
National Institute of Materials Physics, National Institute of Optoelectronics
2012
|
| Online-ссылка: | http://psasir.upm.edu.my/id/eprint/52267/1/Microwave%20irradiation%20effects%20on%20hydrothermal%20and%20polyol%20synthesis%20of%20ZnS%20nanoparticles.pdf |
| Метки: |
Добавить метку
Нет меток, Требуется 1-ая метка записи!
|
| Итог: | Cubic structure of spherical ZnS nanoparticles with relatively small size and narrow size distribution were synthesized via microwave-hydrothermal (M-H) and microwave-polyol (M-P) methods from zinc acetate and thioacetamide as starting materials. Distilled water and ethylene glycol were used as solvents for the M-H and M-P method respectively. To monitor the effect of microwave irradiation, the reactions were carried out in different irradiation time from 5 to 40 min. An increase in irradiation time increases the reaction yield and the average particle size, which subsequently decreases the optical band gap. ZnS nanoparticles synthesized by M-H method have narrower size distribution between 3 and 7 nm, while those synthesized by M-P method were between 2 and 9 nm. Moreover, the formation of hierarchical nanoballs ZnS were observed in the M-H method after 25 min irradiation time. Because of lower dielectric constant, higher dielectric loss, and higher boiling point of ethylene glycol compared to water, in the M-P method the heating rate and final temperature are higher than in M-H method, leading to the decomposition of thiocetamide, promoting higher rate of nucleation. ZnS nanocrystals synthesized with the polyol method have a higher degree of crystallinity compare with those synthesized using the hydrothermal method. |
|---|